Page 59 - IJB-5-2
P. 59
Shuai C, et al.
A B
C D
Figure 5. Immersion degradation behaviors of AZ61-Ti: (A) Hydrogen evolution volumes, (B) pH during immersion, (C) ion-releasing
behavior during immersion, and (D) corrosion rate calculated from the mass loss.
A B
C D
E F
Figure 6. Corrosion surfaces of (A) AZ61, (B) AZ61-0.25Ti, (C) AZ61-0.5Ti, (D) AZ61-0.75Ti, and (E) AZ61-1.0Ti observed under
scanning electron microscope after immersion for 2 and 7 days; (F) energy dispersive spectroscopy results of specific areas in AZ61-0.5Ti.
International Journal of Bioprinting (2019)–Volume 5, Issue 2 55